Method of manufacturing a sonos device

ABSTRACT

A SONOS device and a method of manufacturing the same is provided. A tunnel dielectric layer, a charge trap layer, and a charge blocking layer are formed on a semiconductor substrate, and the charge blocking layer is formed on the charge trap layer such that the charge blocking layer is relatively thicker at regions adjacent to or overlapping the source and the drain and relatively thinner at a region overlapping the channel region. A gate is then formed on the blocking layer.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority to and the benefit of Korean PatentApplication No. 10-2004-0117148 filed in the Korean IntellectualProperty Office on Dec. 30, 2004, the entire contents of which areincorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semiconductor device. Moreparticularly, the present invention relates to aSilicon-Oxide-Nitride-Oxide-Silicon (SONOS) device in which protectionfrom rupture of an Oxide-Nitride-Oxide (ONO) layer with a charge traplayer is enhanced, and a method of manufacturing the same.

2. Description of the Related Art

SONOS devices are considered to be very important as non-volatile memorydevices. However, one significant problem with this type of devices isthat for write and erase operations they require application of a highvoltage that may ultimately destroy the ONO layer with the charge traplayer.

FIG. 1 is a cross-sectional view of a conventional SONOS device.

Referring to FIG. 1, in a conventional SONOS device an ONO structure 20is formed on a silicon substrate 10. The ONO structure 20 includes atunnel oxide layer 21, a silicon nitride layer 23, and a silicon oxidelayer 25 for charge blocking. A conductive polysilicon layer isdeposited on the ONO structure 20 to form a gate electrode 30. A source41 and a drain 45 are formed on the substrate 10 adjacent to the gateelectrode 30, thereby completing a transistor structure.

When a positive (+) voltage is applied to the gate electrode 30,electrons are transferred to the silicon surface. If a higher voltage isapplied to the gate electrode 30, some of the electrons obtainsufficient energy and they move through the tunnel oxide layer 21 by FNtunneling. The electrons that move through the tunnel oxide layer 21 aretrapped in the nitride layer 23 in the ONO structure 20. Therefore,during a write operation, negative charges 27 are trapped in the siliconnitride layer 23.

Because of the electrons trapped in the nitride layer 23, as theapplication of the high voltage to the gate electrode 30 continues, thevoltage measurement increases to the transistor threshold voltage (Vth)causing the transistor to turn off, thereby terminating the programoperation. In an attempt to improve such a program characteristic, priorart techniques have tried to form the ONO layer to be extremely thinsuch that the amount of electrons undergoing FN tunneling may beincreased. A thin ONO structure 20, however, is easily ruptured at ahigh voltage. Furthermore, changing of the nitride layer characteristichas also been tried for improving the program characteristic.

Additionally, while during the program operation, the electrons in theregion where the source 41 and the drain 45 overlap with the gateelectrode 30 are transferred to the nitride layer 23, during an eraseoperation, such electrons may not easily escape to the channel region.This causes the overlap region to become unnecessarily charged withelectrons. In turn, this phenomenon may cause the ONO layer 20 to bedestroyed due to continual degradation of the ONO layer 20 byprogram-erase stress.

SUMMARY OF THE INVENTION

The present invention provides a SONOS device and method ofmanufacturing the same that substantially obviates one or more of theproblems due to limitations and disadvantages of the related art.

One advantage of the present invention is that it can prevent rupture ofan ONO structure used as a charge trap layer.

An exemplary SONOS device according to an embodiment of the presentinvention includes: a source and a drain formed with a channeltherebetween on a semiconductor substrate; a tunnel dielectric layerformed on the semiconductor substrate; a charge trap layer formed on thetunnel dielectric layer; a charge blocking layer formed on the chargetrap layer such that the charge blocking layer is relatively thicker atregions adjacent to or overlapping the source and the drain and isrelatively thinner at a region overlapping the channel between therelatively thicker regions; and a gate formed on the charge blockinglayer.

The tunnel dielectric layer may include a silicon oxide layer, thecharge trap layer may include a silicon nitride layer, and the chargeblocking layer may include a silicon oxide layer.

An exemplary method of manufacturing a SONOS device according to anembodiment of the present invention includes: forming a tunneldielectric layer on a semiconductor substrate; forming a charge traplayer on the tunnel dielectric layer; forming a charge blocking layer onthe charge trap layer such that the charge blocking layer is relativelythicker at regions adjacent to or overlapping source and drain regionsand is relatively thinner at a region overlapping a channel regionbetween the source and drain regions; and forming a gate on the chargeblocking layer.

Formation of the charge blocking layer may include: forming a firstcharge blocking layer on the charge trap layer; selectively etching aregion of the first charge blocking layer overlapping the channel;forming a second charge blocking layer on the etched first chargeblocking layer, the second blocking layer having locally thicker regionswhere the steps are formed by the etching of the first charge blockinglayer; and patterning the second charge blocking layer such that thelocally thicker regions may be adjacent to or overlap the source and thedrain.

Selectively etching the first charge blocking layer may include: forminga mask exposing the region of the first charge blocking layeroverlapping the channel; and selectively etching the first chargeblocking layer exposed by the mask, such that the lower charge traplayer is exposed.

Selectively etching the first charge blocking layer may be performed byremoving the exposed region of the first charge blocking layer using themask such that the lower charge trap layer is exposed.

It is to be understood that both the foregoing general description andthe following detailed description are exemplary and explanatory and areintended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are included to provide a furtherunderstanding of the invention and are incorporated in and constitute apart of this specification, illustrate exemplary embodiments of theinvention and together with the description serve to explain theprinciple of the invention.

In the drawings:

FIG. 1 is a cross-sectional view of a conventional SONOS device.

FIG. 2 to FIG. 5 are cross-sectional views of a SONOS device showingsequential stages of a method of manufacturing the same according to anexemplary embodiment of the present invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Reference will now be made in detail to an exemplary embodiment of thepresent invention, examples of which are illustrated in the accompanyingdrawings.

In an exemplary embodiment of the present invention, a method forlocally thickening the region of an ONO structure in which a gate isoverlapped with a source and a drain is provided. In this exemplaryembodiment, rupture characteristics of the ONO structure may beimproved.

According to an embodiment of the present invention, an ONO layer isdeposited, and then a part of a region of the uppermost oxide layer isremoved. Another oxide layer is then separately deposited thereon toform an uppermost oxide layer. Therefore, the thickness of the portionof the ONO structure overlapping with the channel region can remain thesame as in a conventional device; however, the thickness of the portionof the ONO structure overlapping or adjacent to the source and the drainis relatively larger.

When the SONOS transistor performs an erase operation by applying anegative voltage to the gate electrode, the amount of undesiredelectrons which move from the gate electrode to the nitride layerthrough the uppermost oxide layer by back-tunneling steeply decreases inthe portions where the locally thicker regions of the ONO structureoverlaps or is adjacent to the source and the drain. Accordingly, theamount of electrons accumulated in the locally thicker regionssubstantially decreases. Therefore, rupture of the ONO layer can besuppressed very effectively when the write and erase operations areperformed repeatedly.

FIG. 2 to FIG. 5 show cross-sectional views of a SONOS device showingsequential stages of a method of manufacturing the same according to anexemplary embodiment of the present invention.

Referring to FIG. 2, an oxide layer to be used as a tunnel dielectriclayer 210 is formed on a semiconductor substrate 100 (e.g., a siliconsubstrate) by a deposition method or by oxidization of the siliconsubstrate. A well, for example a p-well, may be formed in the siliconsubstrate prior to the formation of the tunnel dielectric layer. Thetunnel dielectric layer 210 may be formed of a thickness of about 20 Å.A silicon nitride layer is formed as a charge trap layer 230 on thetunnel dielectric layer 210. A silicon oxide layer is then formed as thefirst charge blocking layer 250 on the silicon nitride layer.

Referring to FIG. 3, a part of the first charge blocking layer 250 isselectively removed. A mask 300, which exposes a part of the firstcharge blocking layer 250, is formed on the first charge blocking layer250. A photoresist pattern exposing the region of the first chargeblocking layer 250 that overlaps the channel region may be formed on thefirst charge blocking layer 250 and used as the mask 300. The exposedregion of the first charge blocking layer 250 is then selectivelyremoved using the mask 300 as an etching mask.

Referring to FIG. 4, after a part of the first charge blocking layer 250is selectively removed by etching, a second charge blocking layer 270 isformed on the first charge blocking layer 250. The second chargeblocking layer may be a silicon oxide layer or the like. Hence, thesecond charge blocking layer 270 has steps such that relatively thickerand thinner portions may be formed on the charge trap layer 230. In thestep regions, the second charge blocking layer 270 is thicker.

Referring to FIG. 5, a conductive polysilicon layer is formed on thesecond charge blocking layer 270, and then a gate electrode 400 isformed by a patterning process. In this case, the lower ONO structure200 can be patterned separately or it can be patterned together with thegate electrode 400.

Subsequently, a source 510 and a drain 550 are formed by implantingimpurities into the semiconductor substrate 100 adjacent to the gateelectrode 400 by ion implantation. The source and drain 510 and 550 mayalso be formed to overlap a part of the terminal of the gate electrode400. This can improve the operation of SONOS devices.

When the lower ONO structure 200 is patterned, the second chargeblocking layer 270 is also patterned at the same time such that therelatively thicker region of the second charge blocking layer 270 canremain. Therefore, the thickness of the portion of the ONO structure 200located at the region of the source and drain 510 and 550 overlappingthe gate electrode 400 becomes relatively thicker in comparison with theportion of the ONO structure 200 located over the channel region.

This can significantly decrease the probability of charge trapping inthe local regions when the SONOS device undergoes the write and eraseoperations at a high voltage, so it can dramatically decrease the amountof charge accumulated during the write and erase operations.Accumulation of the electric field from the accumulated charge alsodecreases, and thus, endurance characteristics (i.e., a characteristicof a repetition of the write and erase operations) can be improved.Therefore, the rupture phenomenon in the ONO structure 200 can beimproved.

According to an embodiment of the present invention, the thickness ofthe charge blocking layer located over the region of the source anddrain 510 and 550 overlapping the gate electrode 400 is thicker comparedto that of the charge blocking layer 270 located over the channelregion, so the probability of charge trapping over the source anddraining region can be dramatically decreased when the SONOS deviceundergoes the write and erase operations at a high voltage.

It will be apparent to those skilled in the art that variousmodifications and variations can be made in the present inventionwithout departing from the spirit or scope of the invention. Thus, it isintended that the present invention cover the modifications andvariations of this invention provided they come within the scope of theappended claims.

1. A SONOS device, comprising: a semiconductor substrate; a source and adrain formed with a channel therebetween on the semiconductor substrate;a tunnel dielectric layer formed on the semiconductor substrate; acharge trap layer formed on the tunnel dielectric layer; a chargeblocking layer formed on the charge trap layer such that the chargeblocking layer is relatively thicker at regions adjacent to oroverlapping the source and the drain and relatively thinner at a regionoverlapping the channel between the relatively thicker regions; and agate formed on the charge blocking layer.
 2. The SONOS device of claim1, wherein: the tunnel dielectric layer comprises a silicon oxide layer;the charge trap layer comprises a silicon nitride layer; and the chargeblocking layer comprises a silicon oxide layer. 3-8. (canceled)
 9. TheSONOS device of claim 1, wherein: the tunnel dielectric layer includesan oxide layer by a deposition method or by oxidation of the siliconsubstrate.
 10. The SONOS device of claim 1, wherein: the semiconductorsubstrate includes p-well or n-well.
 11. The SONOS device of claim 1,wherein: the tunnel dielectric layer is formed of thickness of 20 Å˜100Å.
 12. The SONOS device of claim 1, wherein: the charge trap layerincludes a silicon nitride layer.
 13. The SONOS device of claim 1,wherein: the charge blocking layer includes a silicon oxide layer. 14.The SONOS device of claim 1, wherein: the source and drain are formed tooverlap a part of the terminal of the gate electrode.